ANALISA SIFAT MEKANIK PAPAN PARTIKEL DARI SERAT AMPAS TEBU DENGAN RESIN POLYESTER

Eky, Pratama Ridwan (2020) ANALISA SIFAT MEKANIK PAPAN PARTIKEL DARI SERAT AMPAS TEBU DENGAN RESIN POLYESTER. Diploma thesis, UNIVERSITAS BUNG HATTA.

	Text 10 Eky Pratama Ridwan (1610017211008) COVER.pdf Download (19kB)
	Text 10 Eky Pratama Ridwan (1610017211008) ABSTRAK.pdf Download (14kB)
	Text 10 Eky Pratama Ridwan (1610017211008) BAB I.pdf Download (882kB)
	Text 10 Eky Pratama Ridwan (1610017211008) BAB II.pdf Restricted to Repository staff only Download (1MB)
	Text 10 Eky Pratama Ridwan (1610017211008) BAB III.pdf Restricted to Repository staff only Download (975kB)
	Text 10 Eky Pratama Ridwan (1610017211008) BAB IV.pdf Restricted to Repository staff only Download (1MB)
	Text 10 Eky Pratama Ridwan (1610017211008) BAB V.pdf Restricted to Repository staff only Download (848kB)
	Text 10 Eky Pratama Ridwan (1610017211008) DAFTAR PUSTAKA.pdf Download (18kB)

Abstract

Serat ampas tebu merupakan bahan sisa berserat dari batang tebu yang telah mengalami ekstraksi niranya dan banyak dimanfaatkan sebagai bahan baku partikel untuk papan komposit. Dimana serat ampas tebu digunakan sebagai penguat dan resin polyester dan hardener sebagai matrik dari komposit tersebut. Untuk pembentukan material komposit ini telah diatur komposisinya yaitu : 8:92, 10:90, dan 12:88 dengan susunan acak Wt%. Berdasarkan hasil dari penelitian ini didapatkan nilai rata-rata terbaik kekuatan impact pada komposisi 12%:88% sebesar 9,6579 J/mm 2 sedangkan yang nilai terendah pada komposisi 8%:92% sebesar 8,3628 J/mm 2 . Nilai kekuatan lentur terbaik terlihat pada komposisi 8%:92% sebesar 123,29555 Mpa sedangkan yang terendah 12%:88% sebesar 98,2 Mpa dan kekuatan tarik 2 sedangkan terendahnya pada komposisi 12%:88% sebesar 22,563 N/mm Kata kunci : Ampas tebu, Polyester, Hardener, Papan partikel, Uji impak, Uji lentur, Uji tarik.