ANALISA KEKUATAN TARIK KAWAT ALUMINIUM HASIL PROSES WIRE DRAWING MELALUI DIES SUDUT KEMIRINGAN 10°

Budi, Karisma and Iqbal, Iqbal and Wenny, Marthiana (2021) ANALISA KEKUATAN TARIK KAWAT ALUMINIUM HASIL PROSES WIRE DRAWING MELALUI DIES SUDUT KEMIRINGAN 10°. Diploma thesis, UNIVERSITAS BUNG HATTA.

	Text 50 BUDI KARISMA 1510017211026 Cover.pdf Download (84kB)
	Text 50 BUDI KARISMA 1510017211026 Abstrak.pdf Download (133kB)
	Text 50 BUDI KARISMA 1510017211026 BAB I.pdf Download (173kB)
	Text 50 BUDI KARISMA 1510017211026 BAB II.pdf Restricted to Registered users only Download (457kB)
	Text 50 BUDI KARISMA 1510017211026 BAB III.pdf Restricted to Registered users only Download (728kB)
	Text 50 BUDI KARISMA 1510017211026 BAB IV.pdf Restricted to Registered users only Download (731kB)
	Text 50 BUDI KARISMA 1510017211026 BAB V.pdf Restricted to Registered users only Download (149kB)
	Text 50 BUDI KARISMA 1510017211026 Daftar Pustaka.pdf Download (136kB)

Abstract

Penelitian ini bertujuan untuk mendapatkan kawat dengan kekuatan yang tinggi agar kawat tidak mengalami putus ketika digunakan. Perlu dilakukan analisis kekuatan yang di miliki suatu kawat sehingga memiliki daya guna dan dapat dimanfaatkan. Peneliti melakukan uji kekuatan tarik kawat aluminium hasil proses wire drawing melalui sudut kemiringan 10°. Berdasarkan hasil pengujian diketahui bahwa proses wire drawing melalui dies dengan sudut kemiringan 10° mereduksi kawat aluminium sebesar 25%. Kemudian hasil reduksi tersebut dilakukan uji tarik dan menghasilkan nilai kekuatan tarik sebesar 410,47 Mpa dan menghasilkan nilai kekuatan luluh sebesar 368,01 Mpa. Uji tarik kawat aluminium dari hasil proses wire drawing menghasilkan nilai gaya tarik Fu sebesar 2,9 kN atau 2900 N dan gaya tarik Fy sebesar 2,6 kN atau 2600 N. Selanjutnya reduksi 25% hasil proses wire drawing menghasilkan regangan sebesar 12% pada kawat aluminium. Kata Kunci: aluminium, wire drawing, reduksi, uji tarik.