Roberto, Roberto and Burmawi, Burmawi and Kaidir, Kaidir (2021) ANALISA KEKERASAN MATERIAL BIOKOMPOSIT HIDROKSIAPATIT BOROSILIKAT DENGAN TEKANAN 30,40,50 KG/CM² DAN TEMPERATUR SINTERING 1000°C. Diploma thesis, UNIVERSITAS BUNG HATTA.
|
Text
36 ROBERTO 1410017211112 Cover.pdf Download (78kB) | Preview |
|
|
Text
36 ROBERTO 1410017211112 Abstrak.pdf Download (56kB) | Preview |
|
|
Text
36 ROBERTO 1410017211112 BAB I.pdf Download (138kB) | Preview |
|
![[img]](http://repo.bunghatta.ac.id/style/images/fileicons/text.png) |
Text
36 ROBERTO 1410017211112 BAB II.pdf Restricted to Registered users only Download (640kB) |
|
|
Text
36 ROBERTO 1410017211112 BAB III.pdf Restricted to Registered users only Download (201kB) |
|
|
Text
36 ROBERTO 1410017211112 BAB IV.pdf Restricted to Registered users only Download (246kB) |
|
|
Text
36 ROBERTO 1410017211112 BAB V.pdf Restricted to Registered users only Download (98kB) |
|
|
Text
36 ROBERTO 1410017211112 Daftar Pustaka.pdf Download (96kB) | Preview |
Abstract
One reason for the use of hydroxyapatite as a bone substitute is because its chemical composition is similar to the mineral phase of human bones. The element added in the formation of Hydroxyapatite is Borosilicate (Borax and Silica). For the formation of the test specimen, printing with different compressive forces that is 30 kg / cm², 40 kg / cm², and 50 kg / cm², then sintered at a temperature of 1000 ° C. To determine the hardness value of the hydroxyapatite and borosilicate biocomposites, a Hardness test is carried out using the shore hardness test. From the results of the hardness test obtained the best value in each compressive force, namely the compressive force of 50 kg / cm² obtained at the composition of 80%: 20% with a hardness value of 97.8 SHN, the compressive force of 40 kg / cm² is also found at the composition of 80%: 20% with a hardness value of 97.5 SHN. and at a compressive force of 50 kg / cm², there is an 80%: 20% composition with a hardness value of 97.2 SHN. This gives the conclusion that the increasing borosilicate composition the value of material hardness increases according to the compressive force and sintering temperature provided by not changing the chemical structure of hydroxyapatite. Keywords: Biocomposite, Hydroxyapatite, Hardness Value, Borosilicate, Sintering
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Fakultas Teknologi Industri > Teknik Mesin |
| Depositing User: | Heltree Ivatureza |
| Date Deposited: | 18 Mar 2021 03:04 |
| Last Modified: | 24 May 2021 04:29 |
| URI: | http://repo.bunghatta.ac.id/id/eprint/3166 |
Actions (login required)
 |
View Item |